Title: Desenvolvimento e análise da passivação com dióxido de silício de células solares com campo retrodifusor seletivo
Other Titles: Development and Analysis of the Surface Passivation of Solar Cells with Silicon Dioxide and Selective Back Surface Field
Author: Razera, Ricardo Augusto Zanotto 
Advisor: Moehlecke, Adriano
First advisor-co: Zanesco, Izete
Abstract (native): A passivação das superfícies de células solares é importante para a redução da taxa de recombinação de pares elétron-lacuna e, consequentemente, para o aumento de eficiência. O objetivo deste trabalho foi analisar a qualidade da passivação obtida com oxidação térmica de lâminas de silício grau solar e células solares com base p e campo retrodifusor seletivo, produzindo filmes finos de SiO2. Primeiramente, foi analisada a dependência do tempo de vida dos portadores de carga minoritários com o tempo e temperatura de oxidação para oxidações com e sem adição de cloro. Medidas de curva I-V e resposta espectral foram realizadas para determinar a influência dos parâmetros de oxidação nas características elétricas de células solares. Os resultados relacionados à limpeza do tubo de oxidação mostraram que a introdução de cloro durante a oxidação foi capaz de evitar a diminuição do tempo de vida dos portadores minoritários para lâminas de silício tipo Czochralski para temperaturas de processo maiores que 1000 °C. Em relação a passivação atribuída ao óxido, foi observado que o tempo de vida efetivo dos portadores minoritários aumenta para óxidos mais espessos. O tempo e a temperatura de oxidação que resultaram em maiores eficiências foram de 45 min e 800 °C, apresentando uma camada de SiO2 nas faces frontal e posterior de 53 nm e 10 nm, respectivamente. A melhor célula solar com campo retrodifusor seletivo e com passivação de SiO2 apresentou Jsc = 36,0 mA/cm2, Voc = 598,6 mV e FF = 0,777, correspondendo a uma eficiência de 16,8 %.
Abstract (english): The passivation of silicon solar cell surfaces is important for reducing the recombination rate of electron-hole pairs and, consequently, for improving efficiency. The goal of this work was to analyze the passivation quality obtained with thermal oxidation of solar grade silicon wafers and of solar cells with type p base and selective back surface field, producing thin films of SiO2. First, the dependence of minority carrier lifetime on oxidation time and temperature with and without the addition of chlorine was analyzed. I-V curves and spectral response measurements were conducted to determine the influence of oxidation parameters on the solar cells electrical characteristics. The results related to the oxidation furnace cleaning showed that introducing chlorine during oxidation it was possible to avoid the decline of minority carrier lifetime for silicon of Czochralski type and temperatures higher than 1000 °C. As regarded to the oxide passivation, it was observed that the effective minority carrier lifetime increases for thicker oxides. The oxidation time and temperature that resulted in the highest efficiencies were 45 min and 800 °C, resulting in oxide thicknesses on the front and back surfaces of 53 nm and 10 nm, respectively. The best solar cell with selective back surface field and SiO2 passivation presented Jsc = 36.0 mA/cm2, Voc = 598.6 mV and FF = 0.777, corresponding to an efficiency of 16.8 %.
Keywords: CÉLULAS SOLARES
ÓXIDO DE SILÍCIO
ENGENHARIA DE MATERIAIS
CNPQ Knowledge Areas: ENGENHARIAS
Language: por
Country: Brasil
Publisher: Pontifícia Universidade Católica do Rio Grande do Sul
Institution Acronym: PUCRS
Department: Faculdade de Engenharia
Program: Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
Access type: Acesso Aberto
URI: http://tede2.pucrs.br/tede2/handle/tede/7164
Issue Date: 11-Jan-2017
Appears in Collections:Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais

Files in This Item:
File Description SizeFormat 
DIS_RICARDO_AUGUSTO_ZANOTTO_RAZERA_COMPLETO.pdfTexto Completo2.61 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.