Title: Síntese e caracterização de nanocompósitos poliuretano/dióxido de titânio
Author: Silva, Vinícius Demétrio da 
Advisor: Einloft, Sandra Mara Oliveira
Abstract (native): Devido à grande demanda do mercado atual de materiais poliméricos e de materiais baseados em uma estrutura polimérica, como alguns compósitos e nanocompósitos, torna-se fundamental a busca e o desenvolvimento de novos materiais. Desta forma, neste trabalho foram estudadas experimentalmente a síntese e a caracterização de nanocompósitos de poliuretano/dióxido de titânio, utilizando-se matérias primas comerciais. Nestas reações foram adicionados 0,5%, 1,0%, 2,0%, 3,0%, 5,0%, 7,0% e 10% em massa de dióxido de titânio (TiO2), levando em conta a massa de poliuretano formada na reação da Poli (-caprolactona) diol (PCL) e do 1,6-diisocianato de hexametileno (HDI). Os materiais foram caracterizados por Espectrometria de Infravermelho por Transformada de Fourier (FTIR), Microscopia Eletrônica de Varredura (MEV), Calorimetria Diferencial Exploratória (DSC), Análise Termo-Gravimétrica (TGA) e Análise Termodinâmico-Mecânica (DMA). Pela análise dos resultados obtidos, os materiais que apresentaram melhor desempenho termo-mecânico foram os polímeros com 2,0, 3,0 e 5,0% de TiO2. Apesar de apresentar uma temperatura de degradação inferior aos materiais com quantidades superiores de carga, as adições de 2,0, 3,0 e 5,0% mostraram-se as mais eficientes nos ensaios de tração. Concluiu-se então que os nanocompósitos sintetizados por polimerização in situ apresentaram, de forma geral, propriedades térmicas (temperatura de degradação) e mecânicas superiores ao polímero puro. Ressalta-se, ainda, não haver necessidade de qualquer tratamento prévio na carga comercial utilizada, o que leva a uma redução no custo do processo
Abstract (english): Due to the demand of the current market of polymeric materials and materials based on a polymeric structure, as some composites and nanocomposites, the development of new materials is fundamental. Thus, this work aims to study the synthesis and experimental characterization of nanocomposites polyurethane/titanium dioxide, using commercial raw materials. The nanocomposites were synthesized by in situ polymerization reactions in which an inorganic filler was added, titanium dioxide (TiO2), in the following proportions by weight in relation to the mass obtained from the pure polymer: 0.5%, 1.0%, 2.0%, 3.0%, 5.0%, 7.0% e 10.0%. These reactions were based in poli(-caprolactone) (PCL) and 1,6-diisocyanate hexane (HDI). The materials were characterized by Infrared Spectroscopy Fourier Transform (FTIR), Scanning Electron Microscopy (SEM), Differential Scanning Calorimetry Analysis (DSC), Thermo-gravimetric analysis (TGA) and Thermodynamic and Mechanical Analysis (TDMA). Analyzing the results obtained, the materials that showed better thermo-mechanical performance were the polymers with 2.0, 3.0 and 5.0% of TiO2. Although showing a lower degradation temperature when compared to the materials with 7.0 and 10.0% of TiO2, the additions of 2.0, 3.0 and 5.0% proved to be the most efficient in tensile tests. It can be concluded that the nanocomposites synthesized by in situ polymerization showed, in general, superior thermal properties (degradation temperature) and mechanical properties when compared to the pure polymer. It is noteworthy that there was no need of any kind of treatment in the commercial filler, which leads to a reduction in the cost of the process
Keywords: ENGENHARIA DE MATERIAIS
POLÍMEROS
POLIURETANOS
POLIMERIZAÇÃO
CNPQ Knowledge Areas: CNPQ::ENGENHARIAS
Language: por
Country: BR
Publisher: Pontifícia Universidade Católica do Rio Grande do Sul
Institution Acronym: PUCRS
Department: Faculdade de Engenharia
Program: Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
Citation: SILVA, Vinícius Demétrio da. Síntese e caracterização de nanocompósitos poliuretano/dióxido de titânio. 2012. 83 f. Dissertação (Mestrado em Engenharia e Tecnologia de Materiais) - Pontifícia Universidade Católica do Rio Grande do Sul, Porto Alegre, 2012.
Access type: Acesso Aberto
URI: http://tede2.pucrs.br/tede2/handle/tede/3194
Issue Date: 27-Jan-2012
Appears in Collections:Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais

Files in This Item:
File Description SizeFormat 
436433.pdfTexto Completo3,59 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.