dc.creatorLedesma, Roger Braun-
dc.creator.Latteshttp://lattes.cnpq.br/3775189423054543por
dc.contributor.advisor1Costa, Eleani Maria da-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/8984247070352397por
dc.contributor.advisor-co1Pires, Marçal José Rodrigues-
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/2495957476572303por
dc.date.accessioned2018-05-14T11:48:12Z-
dc.date.issued2018-01-15-
dc.identifier.urihttp://tede2.pucrs.br/tede2/handle/tede/8027-
dc.description.resumoDesenvolver tecnologias para a captura e armazenamento geológico de CO2 tem sido um desafio constante da comunidade científica na busca de soluções que possam reduzir os impactos ambientais provocados pela liberação desde gás na atmosfera. Porém, seu armazenamento em poços depletados de petróleo tem se mostrado o ponto mais desafiador, pois os materiais aplicados nestes poços podem sofrer degradação na presença de CO2 em estado supercrítico e em altas pressões. Este trabalho tem como objetivo avaliar o desempenho da pasta de cimento classe G, utilizada na cimentação e tamponamento dos poços, em condições de armazenamento geológico de carbono com substituição de parte do cimento por materiais pozolânicos. O material utilizado foi as cinzas volantes, oriundas da queima de carvão mineral da Usina Termoelétrica de Candiota, e zeólitas 4A comerciais sintéticas (4A-1 e 4A-2). Os teores utilizados das pozalanas em substituição ao cimento foram 5% e 10% em massa. O meio em que foram submetidas as amostras foi de água saturada com CO2 a 15 MPa de pressão a 90° C por 7 e 14 dias. A Microscopia Eletrônica de Varredura (MEV), a Difração de Raios X (DRX) e o teste de resistência à compressão foram as técnicas de caracterização utilizadas neste trabalho. Os resultados obtidos mostram que o uso de cinzas volantes aumentou aos 14 dias a resistência à compressão das amostras, principalmente para maior a porcentagem de substituição do cimento por este material (10%), porém a camada alterada quimicamente aumentou. Quando utilizadas as zeólitas 4A-1, notou-se uma menor resistência à compressão que a pasta padrão, mas a camada degradada reduziu. No caso das zeólitas 4A-2, foi constatada a perda significativa de resistência à compressão dos 7 para 14 dias, principalmente para a amostra contendo 10% dessa zeolita, sendo que a camada alterada quimicamente também reduziu.por
dc.description.abstractDeveloping technologies for the capture and geological storage of CO2 has been a constant challenge of the scientific community in the search for solutions that can reduce the environmental impacts caused by the release of this gas into the atmosphere. However, its storage in depleted oil wells has been shown to be a very important point, since the materials applied in wells can suffer degradation in the presence of CO2 in the supercritical state and at high pressures. The objective of this work is to evaluate the performance of the class G cement paste used in cementation of wellbore under conditions of geological carbon storage with replacement of part of the cement by pozoanic materials such as fly ash from the fossil fuel burning of the Candiota Thermoelectric Plant, and synthetic zeolites (4A-1 e 4A-2). The contents of the pozalanas used in substitution of the cement were 5% and 10% in weight. The medium in which samples were submitted for degradation tests was CO2 saturated water at 15 MPa pressure and 90 °C for 7 and 14 days. Scanning Electron Microscopy (SEM), XRay Diffraction (XRD) and compressive strength tests were the characterization techniques used in this work. The results showed that the use of fly ash increased the compressive strength of the samples after 14 days, mainly for higher percentage of cement replacement by this material (10%), but its chemical degraded layer increased. In case of zeolites 4A-1 use, a lower compressive strength was observed compared to the standard paste, but the degraded layer was reduced. When zeolites 4A-2 were used significant loss of compressive strength was observed from 7 to 14 days, mainly for the proportion of the mixture of 10% and its degraded layer also reduced.eng
dc.description.provenanceSubmitted by PPG Engenharia e Tecnologia de Materiais ([email protected]) on 2018-05-03T11:34:42Z No. of bitstreams: 1 dissertação Roger versão biblioteca.pdf: 9741593 bytes, checksum: 510807346e33704b6f1650648b1f1b19 (MD5)eng
dc.description.provenanceApproved for entry into archive by Sheila Dias ([email protected]) on 2018-05-14T11:17:02Z (GMT) No. of bitstreams: 1 dissertação Roger versão biblioteca.pdf: 9741593 bytes, checksum: 510807346e33704b6f1650648b1f1b19 (MD5)eng
dc.description.provenanceMade available in DSpace on 2018-05-14T11:48:12Z (GMT). No. of bitstreams: 1 dissertação Roger versão biblioteca.pdf: 9741593 bytes, checksum: 510807346e33704b6f1650648b1f1b19 (MD5) Previous issue date: 2018-01-15eng
dc.formatapplication/pdf*
dc.thumbnail.urlhttp://tede2.pucrs.br:80/tede2/retrieve/171947/disserta%c3%a7%c3%a3o%20Roger%20vers%c3%a3o%20biblioteca.pdf.jpg*
dc.thumbnail.urlhttp://tede2.pucrs.br:80/tede2/retrieve/171976/DIS_ROGER_BRAUN_LEDESMA_COMPLETO.pdf.jpg*
dc.languageporpor
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpor
dc.publisher.departmentEscola Politécnicapor
dc.publisher.countryBrasilpor
dc.publisher.initialsPUCRSpor
dc.publisher.programPrograma de Pós-Graduação em Engenharia e Tecnologia de Materiaispor
dc.rightsAcesso Abertopor
dc.subjectCO2 Supercríticopor
dc.subjectCimento Classe Gpor
dc.subjectDegradação do Cimentopor
dc.subjectCinzas Volantespor
dc.subjectZeólitas 4Apor
dc.subjectArmazenamento Geológico de CO2por
dc.subjectSupercritical CO2eng
dc.subjectCement Class Geng
dc.subjectCement Degradationeng
dc.subjectFly Asheng
dc.subjectZeolites 4Aeng
dc.subjectGeological Storage of CO2eng
dc.subject.cnpqENGENHARIASpor
dc.titleCinzas volantes e zeólitas sintéticas na composição da pasta de cimento classe G e degradação por CO2 em condições de armazenamento geológico de carbonopor
dc.typeDissertaçãopor
dc.restricao.situacaoTrabalho não apresenta restrição para publicaçãopor
Appears in Collections:Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais

Files in This Item:
File Description SizeFormat 
DIS_ROGER_BRAUN_LEDESMA_COMPLETO.pdfROGER_BRAUN_LEDESMA_DIS9.89 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.