Export this record: EndNote BibTex

Please use this identifier to cite or link to this item: https://tede2.pucrs.br/tede2/handle/tede/7904
Full metadata record
DC FieldValueLanguage
dc.creatorCesero, Leonardo de-
dc.creator.Latteshttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4497270P3por
dc.contributor.advisor1Mota, Eduardo Gonçalves-
dc.contributor.advisor1Latteshttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4705811J8por
dc.date.accessioned2018-03-27T12:27:51Z-
dc.date.issued2017-11-24-
dc.identifier.urihttp://tede2.pucrs.br/tede2/handle/tede/7904-
dc.description.resumoA nanotecnologia na Odontologia está presente nos sistemas adesivos e nas resinas compostas, sendo sua aplicação ainda bastante limitada nos materiais dentários. O gesso odontológico é um material amplamente utilizado e a incorporação de nanopartículas de sílica é desconhecida. O objetivo do estudo é avaliar o comportamento das propriedades mecânicas dos gessos odontológicos a partir da adição de nanopartículas de sílica em diferentes concentrações. Foram confeccionadas 180 amostras, sendo 90 para cada gesso (Durone e Fuji Rock). No grupo controle (GC) não foram adicionadas partículas, no grupo teste 1 (GT1) foram adicionadas 1% em peso e o grupo teste 2 (GT2) recebeu 5% em peso de nanopartículas de sílica. Os testes de rugosidade, tração diametral (DTS) e compressão foram realizados após 24 horas do início da espatulação. Os valores médios de rugosidade para o Durone foram de GC= 0,55, GT1= 0,36 e GT2= 0,28 μm e para o Fuji Rock foram de GC= 0,47, GT1= 0,31 e GT2= 0,35 μm. Para DTS foram de GC= 6,03, GT1= 5,17 e GT2= 5,02 MPa para o Durone e para o Fuji Rock foram de GC= 6,41, GT1= 5,23 e GT2= 4,56 MPa. Para compressão foram de GC= 35,44, GT1= 32,70 e GT2= 32,44 MPa para o Durone e para o Fuji Rock foram de GC= 42,97, GT1= 31,22 e GT2= 29,86 MPa. Houve uma menor rugosidade superficial estatisticamente para os gessos Durone e Fuji Rock (p< 0,001) quando adicionadas nanopartículas de sílica. Para a DTS e compressão não houve estatisticamente resultados melhores quando adicionadas nanopartículas de sílica em comparação aos grupos controles (p> 0,05).por
dc.description.abstractThe current applications of nanotechnology in dentistry include adhesive systems and composite resins, but they are still quite limited in dental materials. Dental stone is a widely used material, and the incorporation of silica nanoparticles is still unexplored. The purpose of this study is to evaluate the behavior of the mechanical properties of dental stones with the addition of silica nanoparticles at different concentrations. A total of 180 samples were prepared, 90 for each dental stone (Durone and Fuji Rock). For the control group (CG), no silica particles were added, while test group 1 (TG1) had silica nanoparticles added to 1% by weight, and test group 2 (TG2) had silica nanoparticles added to 5% by weight. The roughness, diametral tensile strength (DTS) and compressive strength were measured 24 hours after the start of spatulation. The mean roughness values for Durone were CG= 0,55, TG1= 0,36 and TG2= 0,28 μm and for Fuji Rock were CG= 0,47, TG1= 0,31 and TG2= 0,35 μm. The mean DTS values for Durone were CG= 6,03, TG1= 5,17 and TG2= 5,02 MPa and for Fuji Rock were CG= 6,41, TG1= 5,23 and TG2= 4,56 MPa. The mean compressive strength values for Durone were CG= 35,44, TG1= 32,70 and TG2= 32,44 MPa and for Fuji Rock were CG= 42,97, TG1= 31,22 and TG2= 29,86 MPa. Surface roughness was statistically lower for the Durone and Fuji Rock stones (p< 0,001) when silica nanoparticles were added. For DTS and compressive strength, the addition of silica nanoparticles did not lead to statistically better results when compared to the control groups (p> 0,05).eng
dc.description.provenanceSubmitted by PPG Odontologia ([email protected]) on 2018-03-15T18:05:08Z No. of bitstreams: 1 LEONARDO_DE_CESERO_TES.pdf: 930355 bytes, checksum: 2c97f9568abe8fdc237aa889661c8a3c (MD5)eng
dc.description.provenanceApproved for entry into archive by Tatiana Lopes ([email protected]) on 2018-03-27T12:23:49Z (GMT) No. of bitstreams: 1 LEONARDO_DE_CESERO_TES.pdf: 930355 bytes, checksum: 2c97f9568abe8fdc237aa889661c8a3c (MD5)eng
dc.description.provenanceMade available in DSpace on 2018-03-27T12:27:51Z (GMT). No. of bitstreams: 1 LEONARDO_DE_CESERO_TES.pdf: 930355 bytes, checksum: 2c97f9568abe8fdc237aa889661c8a3c (MD5) Previous issue date: 2017-11-24eng
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESpor
dc.description.sponsorshipConselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPqpor
dc.formatapplication/pdf*
dc.thumbnail.urlhttp://tede2.pucrs.br:80/tede2/retrieve/171263/LEONARDO_DE_CESERO_TES.pdf.jpg*
dc.languageporpor
dc.publisherPontifícia Universidade Católica do Rio Grande do Sulpor
dc.publisher.departmentEscola de Ciências da Saúdepor
dc.publisher.countryBrasilpor
dc.publisher.initialsPUCRSpor
dc.publisher.programPrograma de Pós-Graduação em Odontologiapor
dc.rightsAcesso Abertopor
dc.subjectGesso Dentáriopor
dc.subjectMateriais Dentáriospor
dc.subjectNanopartículas de Sílicapor
dc.subject.cnpqCIENCIAS DA SAUDE::ODONTOLOGIApor
dc.titleInfluência da adição de nanopartículas de sílica nas propriedades mecânicas de gessos odontológicospor
dc.typeTesepor
dc.restricao.situacaoTrabalho não apresenta restrição para publicaçãopor
Appears in Collections:Programa de Pós-Graduação em Odontologia

Files in This Item:
File Description SizeFormat 
LEONARDO_DE_CESERO_TES.pdfLEONARDO_DE_CESERO_TES908.55 kBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.