Title: Compósitos de poliuretano-ZnO e poliuretano-SiO2 : efeito do método de preparação
Author: Soares, Rafael Ribeiro 
Advisor: Ligabue, Rosane Angélica
Abstract (native): A necessidade de desenvolvimento de novos e diferenciados materiais poliméricos fez com que as atenções fossem voltadas para o estudo de compósitos utilizando cargas inorgânicas usuais. Levando em consideração a grande aplicação dos poliuretanos (PU) e a utilização de dispersões aquosas poliuretanos em diversas áreas, este trabalho teve como objetivo principal o estudo da preparação e caracterização de compósitos de PU com óxido de zinco (ZnO) e sílica proveniente da cinza da casca de arroz (SCCA) em uma dispersão aquosa de poliuretano (DAP). Os compósitos foram preparados com matérias-primas comerciais, onde foi utilizado de dois métodos diferentes: in situ, onde a carga foi adicionada na formação do pré- polímero e por meio mistura física, onde a carga foi adicionada na DAP finalizada. Nestas reações foram adicionados 1 %, 3 % e 5 % m/m de ZnO e de SCCA, levando em conta a massa de poliuretano formada na reação com poliol poliéster e com o diisocianato de isoforona (IPDI). Os compósitos foram caracterizados por espectrometria de infravermelho (FTIR), microscopia eletrônica de varredura (MEV), calorimetria exploratória diferencial (DSC), análise termogravimétrica (TGA) e análise termodinâmico-mecânica (DMA). Pela análise dos resultados obtidos, os compósitos que apresentaram melhor desempenho mecânico foram os preparados in situ com ambas as cargas utilizadas. Todos os compósitos apresentaram temperatura de degradação superior ao PU puro (de no mínimo 20 °C independente do tipo de utilização da carga). Pode-se verificar também que o método in situ proporcionou melhor distribuição da carga inorgânica no filme de poliuretano e, de forma geral, propriedades térmicas (temperatura de degradação) e mecânicas foram superiores ao polímero puro.
Abstract (english): The need of new and different polymeric materials has attracted the attention to the study of composites using inorganic fillers. Considering the wide range of applications of the polyurethanes (PU) and the use of aqueous polyurethane dispersions in several areas, this work aimed to study the preparation and characterization of PU composites with zinc oxide (ZnO) and silica from the ash rice husk (SCA) in an aqueous dispersion of polyurethane (PAD). The composites were prepared with commercial materials, which was used in two different methods: in situ polimerization, where the load was added with the formed prepolymer and by physical mixing, where the load was added to the finished PAD. For these reaction, it was added 1%, 3% and 5% w / w ZnO and SCA, related to the mass of polyurethane formed in the reaction with the polyester polyol and isophorone diisocyanate (IPDI). The composites were characterized by infrared spectroscopy (FTIR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and thermodynamic-mechanical analysis (DMA). By analyzing the results, the composites with better mechanical performance were prepared in situ independent of used load. All composites showed degradation temperature, when compared with the pure PU (at least 20 ° C, regardless of the used load). It was observed that the in situ method provided better distribution of the inorganic filler in the polymer matrix besides that, the thermal properties (degradation temperature) and the mechanical properties were superior than the pure polymer.
Keywords: ENGENHARIA DE MATERIAIS
POLIURETANO - APLICAÇÕES
POLÍMEROS
MATERIAIS - PROPRIEDADES
CNPQ Knowledge Areas: CNPQ::ENGENHARIAS
Language: por
Country: BR
Publisher: Pontifícia Universidade Católica do Rio Grande do Sul
Institution Acronym: PUCRS
Department: Faculdade de Engenharia
Program: Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
Citation: SOARES, Rafael Ribeiro. Compósitos de poliuretano-ZnO e poliuretano-SiO2 : efeito do método de preparação. 2012. 88 f. Dissertação (Mestrado em Engenharia e Tecnologia de Materiais) - Pontifícia Universidade Católica do Rio Grande do Sul, Porto Alegre, 2012.
Access type: Acesso Aberto
URI: http://tede2.pucrs.br/tede2/handle/tede/3212
Issue Date: 27-Jul-2012
Appears in Collections:Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais

Files in This Item:
File Description SizeFormat 
440909.pdfTexto Completo2.9 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.