Title: Avaliação da resistência de união de adesivos universais à dentina
Author: Costa, Daniele Morosini 
Advisor: Spohr, Ana Maria
Abstract (native): O objetivo deste trabalho foi avaliar, in vitro, a resistência de união à tração sobre a dentina dos sistemas adesivos universais Single Bond Universal (3M), All-Bond Universal (Bisco) e One Coat 7 (Coltène), na versão autocondicionante, tendo o Clearfil SE Bond como controle. O terço médio da coroa de 120 dentes incisivos bovinos foi incluído em resina acrílica autopolimerizável e desgastado em um torno mecânico sob refrigeração à água para obter uma superfície plana em dentina. Os sistemas adesivos foram aplicados sobre a dentina de acordo com as instruções dos fabricantes, seguido da aplicação de resina composta Z250 (3M). Trinta corpos de prova foram confeccionados para cada sistema adesivo. Após armazenagem em água destilada a 37º C por 24 h, metade dos corpos de prova de cada grupo foi submetida à 500.000 ciclos de ciclagem mecânica. Todos os corpos de prova foram submetidos ao teste de resistência de união à tração na máquina de ensaio universal EMIC DL-2000 com velocidade de 0,5 mm/minuto. Os resultados foram analisados pela ANOVA de duas vias e o teste de Tukey (α =5%). Houve interação entre os fatores sistema adesivo e ciclagem mecânica (p<0,05). As médias seguidas de mesma letra não diferem estatisticamente para a resistência de união (MPa) medida após 24 h: One Coat 7 = 7,86ª (±2,90), Single Bond Universal = 6,78AB (±2,03), All-Bond Universal = 5,61BC (±2,32), Clearfil SE Bond = 3,53C (±1,89). Após ciclagem mecânica, os sistemas adesivos Clearfil SE Bond, Single Bond Universal e All-Bond Universal mantiveram os valores de resistência de união comparáveis ao período de 24 h, havendo redução significativa para o One Coat 7. Os sistemas adesivos Single Bond Universal, All-Bond Universal e One Coat 7, na versão autocondicionante, tiveram resistência de união à dentina comparável ao sistema adesivo Clearfil SE Bond. Apenas o sistema adesivo One Coat 7 apresentou redução na resistência de união à dentina após ciclagem mecânica.
Abstract (english): The aim of this study was to evaluate, in vitro, the tensile bond strength to dentin of the adhesive systems Single Bond Universal (3M), All-Bond Universal (Bisco) and One Coat 7 (Coltène), in the self-etch mode, taking Clearfil SE Bond as control. The middle portion of 120 bovine teeth were included in a selfcured acrylic resin and abraded in a mechanic lathe with water refrigeration in order to obtain a plane surface in dentin. The adhesives systems were applied on the dentin in accordance with the instructions of the manufacturers, followed by the application of composite resin Z250 (3M). Thirty specimens were obtained for each adhesive system. After immersion in distilled water at 37 oC for 24 hours, half of the specimens were submitted to cyclic loading using 500,000 cycles. For all specimens, the tensile bond strength was determinated in a universal testing machine (EMIC DL-2000) at a cross-head speed of 0.5 mm/minute. The results were analyzed by two-way ANOVA and Tukey’s test (α = 5%). The interaction between the factors adhesive system and cyclic loading was significant (p<0.05). The means followed by the same letter represent no statistical difference for the tensile bond strength (MPa) after 24 h: One Coat 7 = 7.86A (±2.90), Single Bond Universal = 6.78AB (±2.03), All-Bond Universal = 5.61BC (±2.32), Clearfil SE Bond = 3.53C (±1.89). After cyclic loading, the adhesive systems Clearfil SE Bond, Single Bond Universal and All-Bond Universal maintained the bond strength values comparable to 24 h period. There was a significant decrease only for One Coat 7. The adhesive system Single Bond Universal, All-Bond Universal and One Coat 7, in the self-etch mode, had bond strength to dentin comparable to Clearfil SE Bond. Only the adhesive system One Coat 7 decreased the bond strength to dentin after cyclic loading.
Keywords: ADESIVOS DENTÁRIOS
DENTINA
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)
ODONTOLOGIA
CNPQ Knowledge Areas: CIENCIAS DA SAUDE::ODONTOLOGIA
Language: por
Country: Brasil
Publisher: Pontifícia Universidade Católica do Rio Grande do Sul
Institution Acronym: PUCRS
Department: Faculdade de Odontologia
Program: Programa de Pós-Graduação em Odontologia
Access type: Acesso Aberto
URI: http://tede2.pucrs.br/tede2/handle/tede/6799
Issue Date: 29-Feb-2016
Appears in Collections:Programa de Pós-Graduação em Odontologia

Files in This Item:
File Description SizeFormat 
DIS_DANIELE_MOROSINI_COSTA_PARCIAL.pdfTexto Parcial503.79 kBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.