Title: Influência de diferentes materiais e técnicas restauradoras na carga máxima de carregamento em molares tratados endodonticamente
Author: Bromberg, Carolina Ritter 
Advisor: Burnett Junior, Luiz Henrique
Abstract (native): Objetivos: O objetivo deste estudo foi avaliar e comparar in vitro a resistência máxima ao carregamento de molares tratados endodonticamente e restaurados com: inlays ou onlays de Lava Ultimate, resina composta Z350 XT com ou sem pino de fibra de vidro transfixado. Materiais e métodos: Cinquenta terceiros molares hígidos extraídos foram incluídos em acrílico autopolimerizável e divididos em 5 grupos (n = 10 por grupo): H = hígido, ON = onlay, IN = inlay, RC = resina composta, PT = pino de fibra de vidro + Z350 XT. Em seguida, foram realizados os preparos MOD e o tratamento endodôntico. As restaurações indiretas foram confeccionadas através do sistema CAD/CAM CEREC e cimentadas com SingleBond Universal e RelyX Ultimate sob carga de 1 Kg. As restaurações do grupo RC e PT foram realizadas pela técnica incremental e os dois pinos no grupo PT foram transfixados horizontalmente e colados com resina flowable. Após, os corpos de prova foram submetidos a 500.000 ciclos de fadiga mecânica sob carga vertical de 200 N na frequência de 1 ciclo/segundo. Na sequência, foi aplicado o teste de carga máxima de carregamento em máquina de ensaio universal a uma velocidade de 1 mm/min. Após o ensaio mecânico, as falhas foram categorizadas em fratura de assoalho pulpar (irreparáveis) e fraturas de cúspides (reparáveis). Resultados: Os valores médios obtidos foram (médias seguidas de mesma letra não apresentam diferença estatística para ANOVA e Tukey): RC 1680N ± 454 d; PT 2693N ± 372 bc; ON 2922N ± 774 b; IN 2053N ± 313 cd; H 4514N ± 548 a. O padrão de falha predominante para dentes restaurados com onlays, inlays e resina composta direta com ou sem pino foi do tipo irreparável. Conclusão: Molares endodonticamente tratados e restaurados com pinos de fibra de vidro transfixado e resina composta Z350 XT direta apresentam resistência à fratura similar às restaurações indiretas tipo inlay e onlay de Lava Ultimate. Restaurações com pino transfixado horizontalmente possuem a mesma eficácia que as restaurações onlays.
Abstract (english): Objectives: The aim of this in vitro study was to compare the maximal load resistance of endodontically treated molars restored with: inlays or onlays of Lava Ultimate, composite resin Z350 XT with or without fiberglass post. Methods: Fifty sound extracted third molars were embedded in acrylic resin and divided into 5 groups (n = 10 per group): H = healthy, ON = onlay, IN = inlay, RC = composite resin, PT = fiberglass post + Z350 XT. The MOD preparations and endodontic treatment were performed. Indirect restorations were made through CAD/CAM CEREC system and cemented with SingleBond Universal and RelyX Ultimate under load of 1 kg. Restorations of RC and PT groups were performed by incremental technique and the two posts in the PT group were horizontally transfixed and bonded with flowable resin. Then, mechanical loading in all samples were performed in 500.000 cycles at 200 N at a frequency of 1 cycle / second and the maximum load test was performed in a universal testing machine at a speed of 1 mm / min. After the mechanical test, the faults were categorized into pulpal floor fracture (irreparable) and cuspal fracture (repairable). Results: Mean values were (means followed by the same letter show no significant difference to ANOVA and Tukey): RC 1680N ± 454 d; PT 2693N ± 372 bc; ON 2922N ± 774 b; IN 2053N ± 313 cd; H 4514N ± 548 a. The predominant failure pattern for teeth restored with onlays, inlays and direct composite resin with or without post was the irreparable type. Conclusion: Endodontically treated molars restored with transfixed fiberglass post and composite resin have similar fracture resistance to those restored with indirect Lava Ultimate inlay and onlay. Horizontally fiber post restoration has the same efficiency that onlays restoration.
Keywords: MATERIAIS DENTÁRIOS
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)
RESINAS (ODONTOLOGIA)
RESINAS COMPOSTAS
ENDODONTIA
ODONTOLOGIA
CNPQ Knowledge Areas: CIENCIAS DA SAUDE::ODONTOLOGIA
Language: por
Country: Brasil
Publisher: Pontifícia Universidade Católica do Rio Grande do Sul
Institution Acronym: PUCRS
Department: Faculdade de Odontologia
Program: Programa de Pós-Graduação em Odontologia
Access type: Acesso Aberto
URI: http://tede2.pucrs.br/tede2/handle/tede/6579
Issue Date: 20-Jan-2016
Appears in Collections:Programa de Pós-Graduação em Odontologia

Files in This Item:
File Description SizeFormat 
DIS_CAROLINA_RITTER_BROMBERG_PARCIAL.pdfTexto Parcial116.97 kBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.